UGLJIČNI ALATNI ČELIK U7A/U7, C70U, C70W1, C70W2, 1.1520, 1.1620 PREMA PN-H-85020, DIN 17350, ISO 4957.
| standard | Vrsta čelika | ||||||
|---|---|---|---|---|---|---|---|
| Kemijski sastav postotak | |||||||
| C: | mn: | Da: | P: | S: | Cr: | Ni: | Cu: |
| PN | N7E | ||||||
| 0.65 - 0.74 | 0.15 - 0.30 | 0.15 - 0.30 | <0.025 | <0.025 | <0.15 | <0.20 | <0.20 |
| PN | N7 | ||||||
| 0.65 - 0.74 | 0.15 - 0.35 | 0.15 - 0.35 | <0.030 | <0.030 | <0.20 | <0.25 | <0.25 |
| GOST | U7A - U7A | ||||||
| 0.65 - 0.74 | 0.17 - 0.28 | 0.17 - 0.33 | <0.025 | <0.018 | <0.20 | <0.25 | <0.25 |
| GOST | U7 - U7 | ||||||
| 0.66 - 0.73 | 0.20 - 0.40 | 0.15 - 0.35 | <0.030 | <0.028 | <0.20 | <0.25 | <0.25 |
| ISO | C70W1 - C70U - 1.1520 | ||||||
| 0.65 - 0.75 | 0.10 - 0.40 | 0.10 - 0.30 | <0.030 | <0.030 | - | - | - |
| DIN | C70W2 - 1.1620 | ||||||
| 0.65 - 0.74 | 0.10 - 0.35 | 0.10 - 0.30 | <0.030 | <0.030 | - | - | - |
C70U, U7A, C70W1, C70W2 - specifikacija i primjena
Dubinski i površinski kaljeni ugljični čelik s najnižim udjelom ugljika od N12E ugljičnih materijala. Pokazuje visoku otpornost na udarce, udarce i relativno visoku tvrdoću. Ako govorimo o njegovim nedostacima, karakterizira ga niska otpornost na habanje i niska obradivost. N7E se koristi za proizvodnju alata za obradu drva, mekog kamenja, dasaka za rezanje, malih matrica za vruće probijanje, kovačkih čekića. U nekim slučajevima može se koristiti kao zamjena za čelike za opruge
Mehanička svojstva U7A, C70W1, C70W2
Meko stanje – tvrdoća<187 HB Estado endurecido - dureza >57HRC
Toplinska obrada: procesi i temperature:
Omekšavanje, žarenje na 680 - 710 C Reljef, žarenje na 600 - 700 C Temp. Otvrdnjavanje na 780 - 820 C Temp. kaljenje na 170 - 190 C
U navedenim kvalitetama tvrtka opskrbljuje
Vruće valjane šipke C70U, C70W1, C70