UGLJIČNI ALATNI ČELIK U8A, C80W1, 1.1525, AISI W1 PREMA ISO 4957, DIN 17350.

standardima	Vrsta čelika
Kemijski sastav postotak
C:	Da:	mn:	P:	S:	Cr:	Ni:	Cu:
PN	N8E
0.75-0.84	0.15-0.3	0.15-0.3	<0.025	<0.025	<0.15	<0.2	<0.2
PN	N8
0.75-0.84	0.15-0.35	0.15-0.35	<0.030	<0.030	<0.2	<0.25	<0.25
GOST	U8A - U8A
0.75-0.84	0.15-0.33	0.15-0.28	<0.025	<0.018	<0.12	<0.12	<0.2
DIN	C80W1 - 1.1525
0.75-0.85	0.1-0.3	0.1-0.4	<0.020	<0.020	-	-	-
DIN	C80W2 - 1.1625
0.75-0.85	0.1-0.3	0.1-0.35	<0.030	<0.030	-	-	-
ISO	C80U
0.75-0.85	0.1-0.3	0.1-0.4	<0.030	<0.030	-	-	-
ASTM	AISI W1 - UNS T72301
0.7-0.85	0.1-0.4	0.1-0.4	<0.025	<0.025	<0.15	<0.2	<0.2
STAS	OSC8
0.75-0.84	0.15-0.35	0.10-0.35	<0.030	<0.025	<0.2	<0.25	<0.25
SPOJI	F-513
0.7-0.8	0.10-0.25	0.25-0.60	<0.030	<0.030	-	-	-

Čelik U8A, C80W1, C80W2, AISI W1 - opis

Čelik visoke otpornosti na udarce. Ne može se koristiti za bušenje. Glavne karakteristike: Visoka otpornost na udarce Tvrd materijal Nedovoljna otpornost na brušenje

Primjena

Ova se legura naširoko koristi za: bušilice dlijeta bušilice rezače listove tračne pile za drvo pneumatska dlijeta

fizička svojstva

Tvrdoća je najvažnija karakteristika.

Pravilo	Stupanj	Tvrdoća toplinski obrađena [HB Max]	Tvrdoća nakon hlađenja [min HRC]
ISO	TC80	192	-
GOST	Y8A	187	62
GOST	U8A	187	62
list materijala	C80W1	190	64
ANSI	P{0}}/2	202	64
NF	Y80	-	62
SAŠITI	43952	187	61

Ostala svojstva: Gustoća: 7,81g/cm3

Toplinska obrada i plastični radovi

Sljedeći parametri preporučuju se za radnu i toplinsku obradu. Smjernice za radnu i toplinsku obradu: Kovani do 850-1050 stupnjeva C. Omekšavanje do 680-710 stupnjeva C. Otpuštanje naprezanja do 600-700 stupnjeva C. Otvrdnjavanje do { {3}} stupnjeva C. Temperirajte na 180-300 stupnjeva C

Zavarivanje

Alatni čelik ove vrste nije lako zavariti, pa se zavarivanje treba uzeti u obzir samo za popravke: EN 280 MoB, EN 350 B, EN 450 B, EN 600 B, ENS 50 B, ENS 15CrB, ENS 18 WB.